Experimental Testing of Cellular Construction Materials Containing Flax Particles
Résumé
The feasibility of a sustainable non-autoclaved cellular concrete, based on flax vegetable co-products, for the pro-
duction of usable specimen in the lightweight construction field, has been investigated experimentally. The pro-
duced specimen, containing various volume ratios of flax particles with respect to preformulatd Tradical PF70
lime binder of 0, 1, and 2, were lightened by creating a porous structure in the matrix through the addition of
0.3% wt. Aluminium powder (able to react with calcium hydroxide from the binder and result in microscopic
air-bubbles). Fresh and hardened specimen properties, including hydration, fresh density, porosity, hardened den-
sity, compressive and flexural strengths, toughness energy, and dry thermal conductivity at different temperatures,
were assessed for varying flax-to-binder ratios. Results have shown that the addition of Aluminum powder leads
to restrain the setting time delay of binder-based lime. Moreover, the hardened material displays a significant
decrease in specimen density, thereby resulting in a compressive strength level compatible with that required
in the cellular construction materials sector. Results also highlighted the ability of added flax to induce a change
in the specimen from brittle to ductile behavior. Moreover, a high degree of thermal insulation can be achieved,
which makes the cellular specimen based on flax particle suitable as insulated-bearing walls material.